During startup of a Boiling Water Reactor (BWR), the water chemistry and temperature are constantly changing. Special operational practices can be performed to control the dissolved oxygen level using, for example, vacuum deaeration. To assess the impact of startup practice on environmental cracking in the structural materials used in the BWR, a large program was performed to evaluate crack growth at representative environmental conditions for both conventional and vacuum deaeration startup practices. Five alloys were studied: Types 304 and 316 nuclear grade stainless steel, Inconel 600, carbon steel, and A508-2 low alloy steel. Tests were performed using fracture mechanics type specimens with constant load crack growth measured at appropriate stress intensity levels. The program intent was to compare the crack growth rates for the two practices. The results show that normal startup and startup deaeration environments had varied effects. Sensitized Type 304 stainless steel exhibited a decrease in crack growth rate and concomitant decrease in severity of intergranular fracture morphology at the low temperatures under deaeration. In contrast, the Type 316 nuclear grade displayed very little influence of startup deaeration due to its inherent resistance to stress corrosion cracking. Inconel 600 showed up to a factor of five reduction in crack growth rate in the deaeration environment. The response of the carbon steel to deaeration was mixed—limited benefit was seen at low temperature, none was seen at the higher temperature. Finally, the low alloy steel displayed some improvement in behavior at low temperature at the high stress intensity value investigated. In summary, the program showed that a modest benefit, in terms of stress corrosion cracking mitigation, could be attributed to deaeration during startup, particulary for Type 304 stainless steel and Inconel 600.
Skip Nav Destination
Article navigation
January 1986
Research Papers
The Effect of BWR Startup Environments on Crack Growth in Structural Alloys
D. A. Hale
D. A. Hale
General Electric Company, Nuclear Systems Technology Operation, San Jose, Calif. 95125
Search for other works by this author on:
D. A. Hale
General Electric Company, Nuclear Systems Technology Operation, San Jose, Calif. 95125
J. Eng. Mater. Technol. Jan 1986, 108(1): 44-49 (6 pages)
Published Online: January 1, 1986
Article history
Received:
August 6, 1985
Online:
September 23, 2009
Citation
Hale, D. A. (January 1, 1986). "The Effect of BWR Startup Environments on Crack Growth in Structural Alloys." ASME. J. Eng. Mater. Technol. January 1986; 108(1): 44–49. https://doi.org/10.1115/1.3225840
Download citation file:
Get Email Alerts
Evaluation of Machine Learning Models for Predicting the Hot Deformation Flow Stress of Sintered Al–Zn–Mg Alloy
J. Eng. Mater. Technol (April 2025)
Blast Mitigation Using Monolithic Closed-Cell Aluminum Foam
J. Eng. Mater. Technol (April 2025)
Irradiation Damage Evolution Dependence on Misorientation Angle for Σ 5 Grain Boundary of Nb: An Atomistic Simulation-Based Study
J. Eng. Mater. Technol (July 2025)
Related Articles
The Benefit of Hydrogen Addition to the Boiling Water Reactor Environment on Stress Corrosion Crack Initiation and Growth in Type 304 Stainless Steel
J. Eng. Mater. Technol (January,1986)
Stress Corrosion Crack Growth Rates in Type 304 Stainless Steel in Simulated BWR Environments
J. Eng. Mater. Technol (January,1986)
Prediction of Materials Damage History From Stress Corrosion Cracking in Boiling Water Reactors
J. Pressure Vessel Technol (February,2000)
Effect of Oxidation Chemistry of Supercritical Water on Stress Corrosion Cracking of Austenitic Steels
ASME J of Nuclear Rad Sci (January,2016)
Related Proceedings Papers
Related Chapters
Introduction and Definitions
Handbook on Stiffness & Damping in Mechanical Design
Development of Nuclear Boiler and Pressure Vessels in Taiwan
Companion Guide to the ASME Boiler and Pressure Vessel Code, Volume 3, Third Edition
Section III: Subsections NC and ND — Class 2 and 3 Components
Companion Guide to the ASME Boiler and Pressure Vessel Code, Volume 1, Fourth Edition